Synthesis, Structure, and Characterization of Defect-free [Hf6(μ3-O)4(μ3-OH)4(C4H2O4)6] (Hf-UiO-66-Fum)

Publicado en:Zeitschrift Fur Anorganische Und Allgemeine Chemie. 644 (24): 1771-1776 - 2018-12-31 644(24), DOI: 10.1002/zaac.201800338

Autores: Jacobsen, Jannick; Gosch, Jonas; Stock, Norbert

Afiliaciones

Resumen

The reaction of HfCl4 with fumaric acid (C4H4O4, H(2)Fum) in a DMF/HCOOH solvent mixture at 120 degrees C for 24 h results in the formation of a defect-free sample of Hf-UiO-66-Fum with UiO-66 structure type. Treatment of the (as)-synthesized sample in boiling ethanol followed by a thermal treatment at 70 degrees C leads to a sample of composition [Hf-6(mu(3)-O)(4)(mu(3)-OH)(4)(Fum)(6)]center dot 18H(2)O center dot 2EtOH. In the crystal structure the hexanuclear clusters {Hf-6(mu(3)-O)(4)(mu(3)-OH)(4)} are twelve-fold connected by C4H2O42- ions to form the framework with the fcu topology. This cluster connectivity was confirmed by a combination of characterization techniques methods, i.e. CHN analyses, N-2 sorption as well as H-1-NMR spectroscopic and thermogravimetric measurements. The MOF shows a thermal stability of T = 390 degrees C, a specific BET surface area of 389 m(2)center dot g(-1) and a water uptake of 204 mg center dot g(-1). The crystal structure was determined from powder X-ray diffraction (PXRD) data, employing the Rietveld method. The compound crystallizes in the cubic space group Pn3 and is isostructural to Zr-UiO-66-Fum. Only a small increase of the lattice parameter a from 17.8309(4) to 17.87978(14) angstrom is observed.